Haynes® 25 (L-605)

---

Applications

Combustor liners, furnace liners, gas turbine rotors, nozzle diaphragm valves, springs, heart valves

Description

Haynes^® 25/L605 is a nonmagnetic, Cobalt-Nickel-Chromium-Tungsten alloy that combines excellent high temperature strength with good resistance to oxidization and carburization in environments up to 980°C (1795°F) for long exposures. It also has excellent resistance to sulphidation. Haynes^® 25/L605 responds very well to cold working. 

Industries Supplied

Aerospace, Land-Based Turbines, Power Generation, Electronics, and Medical.

Nominal Composition

C: 0.05 – 0.15
C: 0.05 – 0.15
Mn: 1.0 – 2.0
Si: 0.40 max
P: 0.040 max
S: 0.030 max
Cr: 19.0 – 21.0
Ni: 9.0 – 11.0
W: 14.0 – 16.0
Fe: 3.0 max
Co: balance

Physical Properties

Density: 0.33 lb/in³, (9.1 g/cm³)

Modulus of Elasticity (E): 
At 70°F (20°C): 32.6 x 103 ksi (225 GPa)

Modulus of Rigidity (G): 
At 70°F (20°C): 14.2 x 10³ ksi (98 GPa)

Coefficient of Expansion:
6.8 µin/in.-°F (70°F to 600°F)
12 µm/m-°C (20°C to 538°C)

Electrical Resistivity: 34.9 µΩ.in, (89 µΩ.cm)

Thermal Conductivity: 65 Btu-in/ft²hr-°F, (9.4 W/m-K)

Applicable Specifications

Strip and Foil: AMS 5537, Rolls Royce MSRR 7053, NACE MR0175/ISO 15156

Typical Mechanical Properties

• Annealed
  • Tensile Strength: 130 ksi (896 MPa) Min

---

Haynes^® is a registered trademark of Haynes International, Inc.